Structures by: Hervieu M.
Total: 281
Lanthanum barium copper oxide (1/2/3/6.7)
Ba2Cu3LaO6.7
Comptes Rendus Hebdomadaires des Seances de l'Academie des Sciences, Serie C, Sciences Chimiques (1966-) (1987) 305, 1063-1068
a=3.895Å b=3.895Å c=11.727Å
α=90° β=90° γ=90°
Tantalum phosphorus pentoxide - β
O5PTa
Journal of Solid State Chemistry (1986) 65, 331-342
a=13.07(1)Å b=5.281(4)Å c=13.24(1)Å
α=90° β=120.4° γ=90°
Barium lanthanum copper oxide (1/4/5/13.16)
BaCu5La4O13.16
Journal of Solid State Chemistry (1987) 68, 143-152
a=8.6475(1)Å b=8.6475(1)Å c=3.8594(1)Å
α=90° β=90° γ=90°
Bismuth barium strontium iron oxide (3/1/6/3/16)
BaBi3Fe3O16Sr6
Journal of Solid State Chemistry (1995) 118, 227-240
a=3.837(1)Å b=3.837(1)Å c=61.15999(1000)Å
α=90° β=90° γ=90°
Hexastrontium trineodymium pentacopper copper(III) oxide
Cu6Nd3O17Sr6
Journal of Solid State Chemistry (1991) 91, 41-46
a=3.7547(1)Å b=11.4882(4)Å c=20.0976(7)Å
α=90° β=90° γ=90°
Thallium molybdenum strontium copper carbonate oxide (0.8/0.2/4/2/1/7)
CCu2Mo0.2O10Sr4Tl0.8
Physica C (Amsterdam) (152,1988-) (1995) 254, 33-43
a=3.8251(2)Å b=3.8251(2)Å c=16.42899(100)Å
α=90° β=90° γ=90°
Thallium chromium strontium copper carbonate nitrate oxide (0.85/0.15/4/2/0.5/0.5/7)
C0.5Cr0.15Cu2N0.5O10Sr4Tl0.85
Chemistry of Materials (1,1989- (1997) 9, 2205-2211
a=3.8320(1)Å b=3.8320(1)Å c=16.41119(50)Å
α=90° β=90° γ=90°
Thallium strontium copper iron(III) carbonate oxide (0.85/4/1.85/0.30/1/7)
CCu1.85Fe0.3O10Sr4Tl0.85
European Journal of Solid State Inorganic Chemistry (1997) 34, 983-990
a=3.8246(1)Å b=3.8246(1)Å c=16.5069(4)Å
α=90° β=90° γ=90°
Barium manganate(IV)
BaMnO3
Materials Research Bulletin (1997) 32, 35-42
a=5.663(1)Å b=5.663(1)Å c=20.95499(300)Å
α=90° β=90° γ=120°
Thallium molybdenum strontium copper oxide (0.8/0.2/2/1/5)
CuMo0.2O5Sr2Tl0.8
Physica C (Amsterdam) (152,1988-) (1995) 254, 33-43
a=3.7511(1)Å b=3.7511(1)Å c=8.939(1)Å
α=90° β=90° γ=90°
Thallium strontium cobalt oxide (0.41/1/1/3.11)
CoO3.111Sr0.9999Tl0.41
Chemistry of Materials (1,1989- (1996) 8, 1482-1489
a=4.95Å b=25.18999Å c=11.66Å
α=90° β=97.76° γ=90°
Lead calcium strontium yttrium copper chromium oxide (1.75/0.2/2/1/2.85/0.15/8)
Ca0.2Cr0.15Cu2.85O8Pb1.75Sr2Y
Journal of Solid State Chemistry (1996) 127, 64-71
a=5.3860(7)Å b=5.4195(7)Å c=15.720(2)Å
α=90° β=90° γ=90°
Mercury bismuth strontium copper oxide (0.5/0.5/2/1/4.92)
Bi0.5CuHg0.5O4.92Sr2
Physica C (Amsterdam) (152,1988-) (1996) 257, 195-209
a=3.7652(1)Å b=3.7652(1)Å c=8.9428(3)Å
α=90° β=90° γ=90°
Mercury cerium barium copper oxide (0.85/0.15/2/1/4.15)
Ba2Ce0.15CuHg0.85O4.15
Materials Research Bulletin (1996) 31, 6 657-663
a=3.8801(2)Å b=3.8801(2)Å c=9.495(1)Å
α=90° β=90° γ=90°
Mercury bismuth strontium lanthanum copper oxide (0.5/0.5/1.5/0.5/1/5)
Bi0.5CuHg0.5La0.5O5Sr1.5
Physica C (Amsterdam) (152,1988-) (1996) 257, 195-209
a=3.7769(1)Å b=3.7769(1)Å c=8.8252(3)Å
α=90° β=90° γ=90°
Thallium bismuth strontium copper oxide (0.65/0.46/1.86/1/4.99)
Bi0.4601CuO4.99Sr1.86Tl0.6499
Physica C (Amsterdam) (152,1988-) (1996) 271, 111-121
a=3.7619(1)Å b=3.7619(1)Å c=8.9984(4)Å
α=90° β=90° γ=90°
Neodymium strontium manganese oxide (0.5/0.5/1/3)
MnNd0.5O3Sr0.5
Solid State Communications (1996) 99, 3 173-177
a=5.431(2)Å b=7.625(2)Å c=5.477(2)Å
α=90° β=90° γ=90°
Dilead distrontium copper(I) iron(III) oxide
CuFeO6Pb2Sr2
Journal of Materials Chemistry (1995) 5, 8 1163-1170
a=5.4604(3)Å b=5.5227(3)Å c=12.2112(6)Å
α=90° β=90° γ=90°
Dilead distrontium copper(I) iron(III) oxide
CuFeO6Pb2Sr2
Journal of Materials Chemistry (1995) 5, 8 1163-1170
a=5.4606(3)Å b=5.5228(3)Å c=12.2112(6)Å
α=90° β=90° γ=90°
Dilead distrontium copper(I) iron(III) oxide
CuFeO6Pb2Sr2
Journal of Materials Chemistry (1995) 5, 8 1163-1170
a=5.4604(3)Å b=5.5227(3)Å c=12.2110(6)Å
α=90° β=90° γ=90°
Thallium chromate strontium coppper oxide (3/1/8/4/16)
CrCu4O20Sr8Tl3
Chemistry of Materials (1,1989- (1996) 8, 865-873
a=3.778(1)Å b=15.244(1)Å c=17.67699(100)Å
α=90° β=90° γ=90°
Calcium gadolinium copper oxide chloride (3.8/2.2/3/8.16/3.84)
Ca3.8Cl3.84Cu3Gd2.2O8.16
Journal of Solid State Chemistry (1996) 127, 315-324
a=3.8865(1)Å b=3.8865(1)Å c=41.827(2)Å
α=90° β=90° γ=90°
Dithallium tribarium dichloride pentaoxide
Ba3Cl2O5Tl2
Materials Research Bulletin (1996) 31, 7 773-780
a=4.3499(2)Å b=4.3499(2)Å c=25.36699(100)Å
α=90° β=90° γ=90°
Thallium strontium copper chromate oxide (3/8/4/1/15.9)
CrCu4O19.9Sr8Tl3
Physica C (Amsterdam) (152,1988-) (1996) 262, 159-167
a=3.7803(1)Å b=15.2573(2)Å c=17.67369(30)Å
α=90° β=90° γ=90°
Thallium niobium oxide (8/27.2/72)
Nb27.2O72Tl8
Journal of Solid State Chemistry (1998) 135, 282-292
a=7.534(7)Å b=12.992(12)Å c=15.555(12)Å
α=90° β=90° γ=90°
Yttrium barium copper palladium oxide (1/2/2.5/.5/7)
Ba2Cu2.5O7Pd0.5Y
Journal of Solid State Chemistry (1988) 73, 610-614
a=3.841(1)Å b=3.883(1)Å c=11.671(3)Å
α=90° β=90° γ=90°
Barium diyttrium palladium oxide
BaO5PdY2
European Journal of Solid State Inorganic Chemistry (1988) 25, 111-117
a=6.523(2)Å b=6.523(2)Å c=5.831(2)Å
α=90° β=90° γ=90°
Dibarium diyttrium copper platinum(IV) oxide
Ba2CuO8PtY2
Europhysics Letters (1987) 4, 1023-1029
a=13.207(2)Å b=5.680(2)Å c=10.321(2)Å
α=90° β=90° γ=90°
Dibismuth distrontium calcium dicopper oxide
Bi2CaCu2O8Sr2
Modern Physics Letters B (1988) 2, 491-500
a=5.4054Å b=5.4016Å c=30.7152Å
α=90° β=90° γ=90°
Lead niobium titanium oxide (2/1.4/0.7/6.7)
Nb1.34O6.67Pb2Ti0.66
Bulletin de la Societe Chimique de France (Vol=Year) (1973) 1973, 2593-2595
a=10.52Å b=10.52Å c=10.52Å
α=90° β=90° γ=90°
STRONTIUM CALCIUM NIOBIUM OXIDE (1/0.3/0.7/3)
Ca0.3333Nb0.6667O3Sr
Journal of Solid State Chemistry (1979) 28, 209-222
a=8.19Å b=8.19Å c=8.209Å
α=90° β=90° γ=90°
CALCIUM STRONTIUM NIOBIUM OXIDE (1.1/0.3/0.7/3)
Ca1.0833Nb.6667O3Sr.25
Journal of Solid State Chemistry (1979) 28, 209-222
a=9.84Å b=5.583Å c=14.176Å
α=90° β=90.783° γ=90°
CALCIUM STRONTIUM NIOBIUM OXIDE (0.6/0.8/0.7/3)
Ca.5833Nb.6667O3Sr.75
Journal of Solid State Chemistry (1979) 28, 209-222
a=9.99Å b=5.73Å c=14.16Å
α=90° β=90° γ=90°
CALCIUM STRONTIUM NIOBIUM OXIDE (1.2/0.1/0.7/3)
Ca1.2333Nb.6667O3Sr.1
Journal of Solid State Chemistry (1979) 28, 209-222
a=11.54Å b=16.04Å c=11.18Å
α=90° β=90° γ=90°
Calcium strontium niobium oxide (1.1/0.3/0.7/3)
Ca1.0833Nb.6667O3Sr.25
Journal of Solid State Chemistry (1979) 28, 209-222
a=5.778Å b=8.052Å c=5.63Å
α=90° β=90° γ=90°
CALCIUM STRONTIUM NIOBIUM OXIDE (0.6/0.8/0.7/3)
Ca.5833Nb.6667O3Sr.75
Journal of Solid State Chemistry (1979) 28, 209-222
a=8.14Å b=8.14Å c=8.147Å
α=90° β=90° γ=90°
RUBIDIUM TRITITANIUM NIOBIUM OXIDE
NbO9RbTi3
Annales de Chimie (Paris) (Vol=Year) (1979) 1979, 339-346
a=6.407Å b=3.797Å c=14.918Å
α=90° β=90° γ=90°
Tungsten oxide hemihydrate
HO3.5W
Materials Research Bulletin (1988) 23, 91-97
a=10.206(3)Å b=10.206(3)Å c=10.206(3)Å
α=90° β=90° γ=90°
Barium manganese iron oxide *
BaFe0.233Mn0.767O2.87
Journal of Solid State Chemistry (1988) 73, 107-117
a=5.687(2)Å b=5.687(2)Å c=14.167(4)Å
α=90° β=90° γ=120°
Barium calcium copper(II,III) thallium oxide (2/2/4/.93/8.84)
Ba2Ca2Cu3O8.84Tl0.93
Comptes Rendus Hebdomadaires des Seances de l'Academie des Sciences, Serie C, Sciences Chimiques (1966-) (1988) 307, 27-32
a=3.844Å b=3.844Å c=15.88Å
α=90° β=90° γ=90°
Distrontium dimanganese pentaoxide
Mn2O5Sr2
Materials Research Bulletin (1985) 20, 479-484
a=5.523(1)Å b=10.761(5)Å c=3.811(1)Å
α=90° β=90° γ=90°
Thallium(I,III) barium calcium copper(III) oxide (1.82/2/1.9/3/10.94)
Ba2Ca1.9Cu3O10.94Tl1.82
Journal of Solid State Chemistry (1988) 74, 428-432
a=3.85Å b=3.85Å c=35.6Å
α=90° β=90° γ=90°
Thallium(III) dibarium calcium dicopper(II,III) oxide
Ba2CaCu2O7Tl
Journal of Solid State Chemistry (1988) 75, 212-215
a=3.833Å b=3.833Å c=12.68Å
α=90° β=90° γ=90°
Lanthanum barium copper oxide (1.5/1.5/3/7.02)
Ba1.5Cu3La1.5O7.02
Physica Status Solidi, Sectio A: Applied Research (1988) 107, 73-84
a=3.9098(1)Å b=3.9098(1)Å c=11.7058(5)Å
α=90° β=90° γ=90°
Yttrium barium copper oxide (1/2/3/7)
Ba2Cu2.98O6.96Y
Physica C (Amsterdam) (152,1988-) (1988) 153, 972-973
a=3.858(1)Å b=3.858(1)Å c=11.585(3)Å
α=90° β=90° γ=90°
Yttrium barium copper oxide (1/2/2.9/7)
Ba2Cu2.93O7Y
Physica C (Amsterdam) (152,1988-) (1988) 153, 972-973
a=3.862(1)Å b=3.862(1)Å c=11.673(3)Å
α=90° β=90° γ=90°
Lithium iron(III) antimony(V) tin(IV) oxide (4.66/4/2/1.22/16) - High form
Fe2Li2.33O8SbSn0.66
Journal of Solid State Chemistry (1984) 51, 44-52
a=3.031(1)Å b=5.045(2)Å c=9.798(6)Å
α=90° β=90° γ=90°
Trilithium iron(III) antimonate
FeLi3O8Sb2
Materials Research Bulletin (1984) 19, 693-699
a=9.017(4)Å b=5.013(2)Å c=9.841(4)Å
α=90° β=90° γ=90°
Calcium ferrate manganate
Ca3Mn3O8.02
Journal of Solid State Chemistry (1984) 53, 398-405
a=5.332(2)Å b=11.13(4)Å c=5.455(2)Å
α=90° β=90° γ=90°
Lithium iron(III) antimony(V) tin(IV) oxide (4.66/4/2/1.32/16) - Low form
Fe4Li4.66O16Sb2Sn1.32
Journal of Solid State Chemistry (1984) 51, 44-52
a=5.950(2)Å b=5.950(2)Å c=9.701(4)Å
α=90° β=90° γ=120°
Lead strontium yttrium calcium copper oxide (.5/2.5/.5/.5/ 2/6.3)
Ca0.5Cu2O6.3Pb0.46Sr2.46Y0.5
Physica C: Superconductivity and Its Applications (Amsterdam, Netherlands) (1989) 159, 3 201-209
a=3.817Å b=3.817Å c=11.907Å
α=90° β=90° γ=90°
Lead strontium neodymium cerium copper oxide (2/2/1/1/3/10.2)
CeCu3NdO10.2Pb2Sr2
Physica C: Superconductivity and Its Applications (Amsterdam, Netherlands) (1990) 167, 1-2 107-111
a=5.442(4)Å b=5.462(4)Å c=36.90(2)Å
α=90° β=90° γ=90°
Yttrium dibarium tricopper hexaoxide
Ba2Cu3O6Y
Zeitschrift für Physik B: Condensed Matter (1987) 69, 1 53-59
a=3.865(1)Å b=3.865(1)Å c=11.852(3)Å
α=90° β=90° γ=90°
Lead barium yttrium strontium copper oxide (.92/.92.1.15/1.15/3/8)
Ba0.92Cu3O8Pb0.92Sr1.15Y1.15
Journal of Solid State Chemistry (1989) 78, 322-325
a=3.842(1)Å b=3.842(1)Å c=27.66(1)Å
α=90° β=90° γ=90°
Thallium(III) praseodymium strontium copper oxide (.8/.6/1.6/1/5)
CuO5Pr0.6Sr1.6Tl0.8
Journal of Solid State Chemistry (1989) 78, 326-328
a=3.741Å b=3.741Å c=8.875Å
α=90° β=90° γ=90°
Thallium lead strontium calcium copper oxide *
Ca0.91Cu2O7Pb0.5Sr2Tl0.59
Physica C (Amsterdam) (152,1988-) (1989) 157, 460-468
a=3.795(1)Å b=3.795(1)Å c=12.094(5)Å
α=90° β=90° γ=90°
Yttrium barium copper iron oxide (1/2/2.8/0.2/6.96)
Ba2Cu2.79Fe0.15O6.96Y
Zeitschrift fuer Physik, B (1984-) (1988) 71, 43-52
a=3.858(1)Å b=3.858(1)Å c=11.585(3)Å
α=90° β=90° γ=90°
Yttrium barium copper iron oxide (1/2/2.8/0.2/6.96)
Ba2Cu2.79Fe0.15O6.96Y
Zeitschrift fuer Physik, B (1984-) (1988) 71, 43-52
a=3.862(1)Å b=3.862(1)Å c=11.673(3)Å
α=90° β=90° γ=90°
Hemicalcium hemilithium hemiiron(III) hemitin(IV) oxide
Ca0.5Fe1.5Li0.5O4Sn0.5
Annales de Chimie (Paris) (Vol=Year) (1987) 12, 23-32
a=9.285(3)Å b=10.869(5)Å c=3.020(1)Å
α=90° β=90° γ=90°
Lead strontium yttrium copper oxide (.5/2.5/1/2/6.6)
Cu2O6.6Pb0.5Sr2.5Y
Journal of Solid State Chemistry (1990) 84, 375-385
a=3.8253(3)Å b=3.8253(3)Å c=11.891(1)Å
α=90° β=90° γ=90°
Barium neodymium cerium iron copper oxide (1/1/.9/1.1/.9/7)
BaCe0.9Cu0.9Fe1.1NdO7
Journal of Solid State Chemistry (1991) 92, 339-351
a=3.9025(1)Å b=3.9025(1)Å c=20.8955(5)Å
α=90° β=90° γ=90°
Thallium(III) barium calcium neodymium copper oxide (0.96/2/0.8/0.2/2/6.86)
Ba2Ca0.8Cu2Nd0.2O6.86Tl0.96
Physica C (Amsterdam) (152,1988-) (1991) 178, 29-36
a=3.85638(5)Å b=3.85638(5)Å c=12.6534(2)Å
α=90° β=90° γ=90°
Thallium(III) barium calcium neodymium copper oxide (0.95/2/0.5/0.5/2/6.86)
Ba2Ca0.5Cu2Nd0.5O6.86Tl0.95
Physica C (Amsterdam) (152,1988-) (1991) 178, 29-36
a=3.87677(5)Å b=3.87677(5)Å c=12.6045(3)Å
α=90° β=90° γ=90°
Thallium(III) strontium lanthanum copper oxide (1/1.4/.6/1/5)
CuLa0.6O5Sr1.4Tl
Physica C (Amsterdam) (152,1988-) (1991) 179, 214-226
a=3.7535(1)Å b=3.7535(1)Å c=8.9038(4)Å
α=90° β=90° γ=90°
Thallium(III) barium neodymium copper oxide (0.96/2/1/2/6.96)
Ba2Cu2NdO6.96Tl0.96
Physica C (Amsterdam) (152,1988-) (1991) 178, 29-36
a=3.91021(5)Å b=3.91021(5)Å c=12.4916(2)Å
α=90° β=90° γ=90°
Thallium(III) strontium lanthanum copper oxide (1.3/1/0.7/1/5)
CuLa0.7O5SrTl1.3
Physica C (Amsterdam) (152,1988-) (1991) 179, 214-226
a=3.7713(1)Å b=3.7713(1)Å c=8.8676(2)Å
α=90° β=90° γ=90°
Bismuth lead distrontium yttrium dicopper oxide
BiCu2O8PbSr2Y
Journal of Solid State Chemistry (1989) 79, 157-168
a=5.385Å b=5.424Å c=30.316Å
α=90° β=90° γ=90°
Thallium barium calcium copper oxide (1.9/2/1.1/2/8)
Ba2Ca1.07Cu2O8Tl1.93
Modern Physics Letters B (1988) 2, 681-687
a=3.86Å b=3.86Å c=29.388Å
α=90° β=90° γ=90°
Strontium neodymium copper oxide (2/1/2/5.8)
Cu2NdO5.76Sr2
Physica C (Amsterdam) (152,1988-) (1990) 167, 483-490
a=3.7701(1)Å b=11.4381(5)Å c=20.0938(9)Å
α=90° β=90° γ=90°
Thallium(III) barium lanthanum copper oxide (1/1.6/2.4/2/9)
Ba1.6Cu2La2.4O9Tl
Physica C (Amsterdam) (152,1988-) (1991) 179, 1-8
a=3.8110(2)Å b=3.8110(2)Å c=31.556(2)Å
α=90° β=90° γ=90°
Thallium(III) strontium lanthanum copper oxide
CuLaO5SrTl
Physica C (Amsterdam) (152,1988-) (1991) 179, 214-226
a=3.7796(1)Å b=3.7796(1)Å c=8.8466(3)Å
α=90° β=90° γ=90°
Strontium dithallate
O4SrTl2
Materials Research Bulletin (1991) 26, 123-128
a=10.0411(2)Å b=11.6975(5)Å c=3.4006(5)Å
α=90° β=90° γ=90°
Mercury tetraoxovanadium barium strontium copper oxide (0.67/0.3/1/1/1/3.34)
BaCuHg0.67O4.66SrV0.33
Physica C: Superconductivity and Its Applications (Amsterdam, Netherlands) (1997) 277, 1-2 119-132
a=3.8523(5)Å b=3.8523(5)Å c=9.077(1)Å
α=90° β=90° γ=90°
Lanthanum manganese oxide (.91/1/3)
La0.9125MnO3
Solid State Communications (1997) 101, 4 277-281
a=7.790(1)Å b=5.526(1)Å c=5.479(1)Å
α=90° β=90.78° γ=90°
Bismuth lead strontium calcium manganese oxide (1.5/0.5/1.53/1.47/2/9)
Bi1.5Ca1.47Mn2O9Pb0.5Sr1.53
Journal of Solid State Chemistry (1997) 132, 420-431
a=5.3594(1)Å b=5.3443(1)Å c=30.976(4)Å
α=90° β=90° γ=90°
Strontium manganese(III) boron oxide (4/3.2/0.8/10)
B0.8Mn3.2O10Sr4
Journal of Solid State Chemistry (1997) 134, 395-408
a=3.7865(1)Å b=15.8540(4)Å c=7.6540(2)Å
α=90° β=90° γ=90°
Thallium barium strontium copper oxide (5/3/5/3/19)
Ba3Cu3O19Sr5Tl5
Journal of Solid State Chemistry (1997) 128, 150-155
a=3.7536(2)Å b=30.631(2)Å c=9.219(1)Å
α=90° β=90° γ=90°
Barium manganese oxide (6.3/24/48)
Ba6.3Mn24O48
Journal of Solid State Chemistry (1997) 132, 239-248
a=18.17299(200)Å b=18.17299(200)Å c=2.836(1)Å
α=90° β=90° γ=90°
Thallium(III) praseodymium strontium copper oxide (.8/.6/1.6/1/5)
CuO5Pr0.6Sr1.6Tl0.8
Journal of Solid State Chemistry (1989) 78, 326-328
a=3.741Å b=3.741Å c=8.875Å
α=90° β=90° γ=90°
Thallium lead strontium calcium copper oxide *
Ca0.91Cu2O7Pb0.5Sr2Tl0.59
Physica C (Amsterdam) (152,1988-) (1989) 157, 460-468
a=3.795(1)Å b=3.795(1)Å c=12.094(5)Å
α=90° β=90° γ=90°
Oxonium tantalum tungsten oxide (1/1/1/6)
H3O7TaW
Bulletin de la Societe Chimique de France (Vol=Year) (1971) 1971, 3939-3943
a=10.39Å b=10.39Å c=10.39Å
α=90° β=90° γ=90°
Oxonium hydrogen tantalum oxide (1/1/2/6)
H4O7Ta2
Bulletin de la Societe Chimique de France (Vol=Year) (1971) 1971, 3939-3943
a=10.58Å b=10.58Å c=10.58Å
α=90° β=90° γ=90°
Ammonium tantalum tungsten oxide (1/1/1/6)
H4NO6TaW
Bulletin de la Societe Chimique de France (Vol=Year) (1971) 1971, 3939-3943
a=10.358(5)Å b=10.358(5)Å c=10.358(5)Å
α=90° β=90° γ=90°
Oxonium tantalum tungsten oxide (1.4/1.4/.6/5.6)
H3.4O7Ta1.4W0.6
Bulletin de la Societe Chimique de France (Vol=Year) (1971) 1971, 3939-3943
a=10.485Å b=10.485Å c=10.485Å
α=90° β=90° γ=90°
Oxonium tantalum tungsten oxide (1.8/1.8/.2/5.2)
H3.8O7Ta1.8W0.2
Bulletin de la Societe Chimique de France (Vol=Year) (1971) 1971, 3939-3943
a=10.55Å b=10.55Å c=10.55Å
α=90° β=90° γ=90°
Lead niobium titanium oxide (2/1.3/.7/6.7)
Nb1.33O6.66Pb2Ti0.66
Bulletin de la Societe Chimique de France (Vol=Year) (1973) 1973, 2593-2595
a=10.52Å b=10.52Å c=10.52Å
α=90° β=90° γ=90°
Tripotassium pentatitanium niobium oxide
K3NbO14Ti5
Journal of Solid State Chemistry (1980) 35, 200-206
a=18.371(6)Å b=3.794(1)Å c=9.199(3)Å
α=90° β=101.21(4)° γ=90°
Tripotassium pentatitanium tantalum oxide
K3O14TaTi5
Journal of Solid State Chemistry (1980) 35, 200-206
a=18.363(2)Å b=3.791(1)Å c=9.174(1)Å
α=90° β=101.28(1)° γ=90°
Trirubidium pentatitanium niobium oxide
NbO14Rb3Ti5
Journal of Solid State Chemistry (1980) 35, 200-206
a=19.073(7)Å b=3.814(1)Å c=9.223(4)Å
α=90° β=100.93(4)° γ=90°
Caesium dititanium niobium oxide
CsNbO7Ti2
Journal of Solid State Chemistry (1980) 32, 161-165
a=9.326Å b=18.412Å c=3.798Å
α=90° β=90° γ=90°
Potassium copper tantalate
CuKO9Ta3
Journal of Solid State Chemistry (1984) 53, 184-192
a=8.862(8)Å b=10.187(10)Å c=7.638(6)Å
α=90° β=90° γ=90°
Ba2Bi2Fe4O11
Ba2Bi2Fe4O11
Journal of Solid State Chemistry (1999) 147, 450-463
a=3.9804Å b=3.9804Å c=16.378Å
α=90° β=90° γ=90°
Ba0.5Bi0.5FeO2.75
Ba0.5Bi0.5FeO2.75
Journal of Solid State Chemistry (1999) 147, 450-463
a=3.9802Å b=3.9802Å c=16.376Å
α=90° β=90° γ=90°
Ba (Fe0.67 Bi0.33) O2.5
BaBi0.33Fe0.67O2.5
Journal of Solid State Chemistry (1999) 147, 45-57
a=4.0937Å b=4.0937Å c=4.0937Å
α=90° β=90° γ=90°
(Ba0.7 Bi0.3) (Fe0.9 Bi0.1) O2.67
Ba0.7Bi0.4Fe0.9O2.67
Journal of Solid State Chemistry (1999) 147, 450-463
a=4.0506Å b=4.0506Å c=4.0506Å
α=90° β=90° γ=90°
(Ba0.57 Bi0.43) (Fe0.96 Bi0.04) O2.7
Ba0.57Bi0.47Fe0.96O2.7
Journal of Solid State Chemistry (1999) 147, 45-57
a=3.9954Å b=3.9954Å c=4.09Å
α=90° β=90° γ=90°
(Ba0.63 Bi0.37) (Fe0.94 Bi0.06) O2.7
Ba0.63Bi0.43Fe0.94O2.7
Journal of Solid State Chemistry (1999) 147, 45-57
a=4.0142Å b=4.0142Å c=4.0845Å
α=90° β=90° γ=90°
(Ba0.89 Bi0.11) (Fe0.74 Bi0.26) O2.555
Ba0.89Bi0.37Fe0.74O2.555
Journal of Solid State Chemistry (1999) 147, 45-57
a=4.0819Å b=4.0819Å c=4.0819Å
α=90° β=90° γ=90°
(Ba0.8 Bi0.2) (Fe0.8 Bi0.2) O2.6
Ba0.8Bi0.4Fe0.8O2.6
Journal of Solid State Chemistry (1999) 147, 45-57
a=4.0685Å b=4.0685Å c=4.0685Å
α=90° β=90° γ=90°
(Ba0.71 Bi0.29) (Fe0.86 Bi0.14) O2.645
Ba0.71Bi0.43Fe0.86O2.645
Journal of Solid State Chemistry (1999) 147, 45-57
a=4.0515Å b=4.0515Å c=4.0515Å
α=90° β=90° γ=90°